Anharmonic Origin of Giant Thermal Displacements in the Metal-Organic Framework UiO-67

Katrine L. Svane, Jessica K. Bristow, Aron Walsh

Research output: Contribution to journalArticlepeer-review

3 Scopus citations


The crystallography of mechanically soft materials such as hybrid organic-inorganic compounds often reveals large thermal displacement factors and partially occupied lattice sites, which can arise from static or dynamic disorder. A combination of ab initio lattice dynamics and molecular dynamics simulations reveals the origin of the giant thermal displacements in the biphenyl-4,4′-dicarboxylate (BPDC) linker in the metal-organic framework UiO-67. The dihedral angle between the two phenyl rings has two equivalent minima at ±31°, which cannot be described by harmonic phonons. Instead, anharmonic switching between the minima results in the experimentally observed large thermal ellipsoids. The switching frequency is found to be similar in the topologically distinct framework IRMOF-10, suggesting that dynamic disorder is a general feature of MOFs based on BPDC and structurally similar linkers.

Original languageEnglish
Pages (from-to)22010-22014
Number of pages5
JournalJournal of Physical Chemistry C
Issue number40
StatePublished - 12 Oct 2017

Bibliographical note

Funding Information:
K.L.S. is funded by ERC programme grant no. 277757, and J.K.B. is funded by the EPSRC (grant no. EP/G03768X/1). The authors acknowledge computing support from the UK national supercomputing service (Archer), via membership of the UK Materials Chemistry Consortium which is funded by EPSRC (EP/L000202), and from the University of Bath computing services (Balena).

Publisher Copyright:
© 2017 American Chemical Society.


Dive into the research topics of 'Anharmonic Origin of Giant Thermal Displacements in the Metal-Organic Framework UiO-67'. Together they form a unique fingerprint.

Cite this